Polyester Powder Coating Glossy

Polyester powder coating is a thermosetting powder coating based on saturated Carboxylated polyester resins especially selected for architectural use, it has good flow and excellent resistance to atmospheric ageing environment. This powder coating product is applicable for electrostatic application.
Product meets most of the international requirements and specifications As Qualicoat [P-1864]

SKU: PF-32-XX

  • spe_5

    SUBSTRATE

    Aluminum
  • spe_5

    COLOR

    Available in almost All Ral Color Range
  • spe_5

    APPEARANCE

    Gloss – [77+/- 7]
  • spe_5

    SPECIFIC GRAVITY [ASTM5965-02] Kg/l

    Approx. 1.500 – 1.600 Kg/L
  • spe_5

    SPREADING RATE [MILEAGE]

    Approx. 10.4 – 11.1 m2/Kg [optimal film thickness @ 60µm]
  • USE
  • PROPERTIES
  • CURING CONDITION
  • SHELF LIFE & STORAGE @ 20°C
  • PACK AVAILABLE
  • SURFACE PREPARATION
  • APPLICATION DATA
  • DRY FILM CHEMICAL & MECHANICAL RESISTANCE

Ideal for outdoor application providing excellent resistance, applicable for all type of aluminum extrusion. Products can be applied to Ferrous and non-Ferrous Substrate

  • Excellent flexibility
  • Mechanical properties
  • UV resistance/excellent weathering resistance
  • Outstanding finishes
  • V. Good corrosion resistance

15-30 Minutes @ 190°C m.t in standard conditions – metal temp. 10-20 Minutes @ 200°C m.t in standard conditions – metal temp 08-16 Minutes @ 210°C m.t in standard conditions – metal temp. [The film obtained maintains its property if the polymerization conditions are respected]

12 months when stored in dry and cool conditions @ 25°C, in original sealed containers

20 Kg cardboard boxes.
[Also available in Big Bags or containers upon request]

For Steel:
All surfaces must be dry, clean and free from contaminators. It is suggested a good substrate cleaning as required (sand blasting – degreasing – phosphatizing or chromed, etc…).
For Aluminum:
In order to obtain optimal anti-corrosion properties, it is advised to apply a chemical pretreatment prior to powder coating application.

Applied by electrostatic corona spraying using classic devices which can provide a negative tension of 60-80 kV. The powder is cured in a suitable convection or combustion, or induction, etc…

All test have been effectuated on UNI 0.5mm thickness panel cured polymerization conditions standards.
Test film thicknes:@80µm.

Test Method Range
Film Thickness ISO2808 80 – 100 µm
Gloss (60°C) ISO2813 70 – 84 gloss
Adhesion Crosshatch 2mm BS EN ISO2409 90 – 100% GTO-0
Adhesion Crosshatch 2mm BS EN ISO2409 90 – 100% GTO-0
Cupping Erichsen ISO1520 7 – 10 mm [No cracking]
Direct Impact [2lbs-½ inch] EN ISO 6272-1 80 – 100 cm [No cracking]
Indirect Impact [2lbs-½ inch] EN ISO 6272-1 80 – 100 cm [No cracking]
Pencil Hardness ISO15184 HB – F
Conical Mandrel DIN EN ISO 6860 5-6 mm

Resistance to common synthetic resistance [72 hrs. in 3% solution]
– No blistering or loss of adhesion no significant change in appearance.
Salt spray resistance [ASTM B117-73] on Chromate Aluminum
– No blistering or loss of adhesion during [2000 hrs.]
Humidity Resistance [ASTM D2247] on Chromate Aluminum
– No blistering or loss of adhesion during [1000 hrs.]