PU WATER BASE WHITE PRIMER 2 PACKS FOR INTERIOR
A waterborne 2 PACKS Polyurethane primer white , based on low solvent content and excellent flow leveling, designed as basecoat on pieces previously sanded . It shows a top performance in terms of covering, drying and hardness, compared to any traditional polyurethane finish.
SKU: WBI 10246DP
-
Viscosity Ford cup4/25oC
200 secs. [±5] -
Color
White -
Weight solids
53% [±2] -
Specific gravity
1.14 kg/L [±0.025]
- Description
- SURFACE PREPARATION
- PRODUCT PREPARATION
- APPLICATION METHODS
- CLEANING
- PACKING & STORAGE
- SAFETY & FLAMMABLE
A waterborne 2 PACKS Polyurethane primer white , based on low solvent content and excellent flow leveling, designed as basecoat on pieces previously sanded . It shows a top performance in terms of covering, drying and hardness, compared to any traditional polyurethane finish. This item has a low VOC less than 3% as an environmental friendly product. [Product is following the LEED certificate CREDIT EQ C4.2, as per the rules 1113 for the architectural coating, it has a VOC less water and exempt in the range of 25 g/l].
All timber species must be fully aged with a moisture content of less than 15%. Surface must be dry, clean and free from contaminations. Natural oil or gum must be removed by solvent cleaning. We suggest a good sanding of the wood substrate before applying [WBI10246 DP]. Apply one or two coats of basecoat according to the desired covering required.
Stir product well with a flat paddle. Thin to required viscosity. For details of spray equipment contact Ritver Technical Services Department.
This product needs Catalyst in order to enhance the physical and chemical properties and to get better hardness and scratch resistance.
CATALYST | CP0101 @ 5% |
WATER | 10% |
Dilution
Product ready for use. Eventually it is possible to dilute with water at 5-10% max
Depends on the finishes required but in general an appropriate rate is between 130 gr / sq. m. The number of coats depends on the surface preparation the porosity of the substrate, and the finishes required.
Following Treatments
By spray gun. The product is ready for use; in winter time it is not advisable to thin down the product but it is recommend to use the pre-heater set between 35°C and 45°C; in warmer times it is advisable to thin down the product from 5% up to 10% max. with water and to use the pre-heater at a max. temperature of 35°C.
The product viscosity generally enables the application of 100-120 micron humid thickness without dripping; it is not advisable to apply higher thickness as film sanding and flow levelling would be impaired. It is possible to apply two coats of LEED10246 DP within 2-3 hrs. without sanding; beyond this time limit, we recommend to comply within 24 hrs. of complete drying and then sand and apply the
following varnish coat. In order to varnish large pore substrates, we recommend thinning with water up to 10% for the first coat and 5% for the following one. Suggested nozzle: for airless 09 fixed or 015 adjustable at 4 atm/bar of pressure; for normal spray gun 2.0 mm. at 3.5-4 atm/bar of pressure.
Check very carefully that the spray-gun does not show any trace whatsoever of solvent from previous applications. It is advisable to wash varnishing tools immediately after use.
SUBSEQUENT TREATMENTS
After drying this product must be over coated with pigmented waterborne top finish.
NOTE
Avoid stacking directly on varnish.
As waterborne varnishing have lesser resistance against aggressive chemical agents compared to traditional varnishes, we recommend to clean the piece with water and neutral detergent. Ammonia and/or alcohol base solutions can seriously damage the film. Should aggressive solutions be spilled such as liquors, and similar drinks and/or very hot beverages like coffee, tea etc., we recommend to clean quickly the surface with cloth soaked in water.
Available in USG, 5USG.
Store in a cool and well ventilated place. Keep away from direct sunlight. Maximum 18 months in unopened container, stored in a cool and dry condition at 25°C.
Gluening
Check the type of glue used before varnishing the pieces with waterborne products: glues having a holding value below B3, can cause the following problems:
-Breakaway of the veneering form the substrate, blistering and ensuing damage of the
varnishing piece
-Pore raising
-Film bleaching caused by re-solubilization of the glue resins into the waterborne varnishing Following coats Comply with the drying time between the basecoat and the finish as pore raising may occur if pores are too much reduced.
Blocking
The product is provided with good resistance against blocking: it is however a thermoplastic varnish, therefore it is necessary to evaluate each time storage and stacking conditions of the varnished piece avoiding the contact in between varnished.
Tannin
Check very carefully the type of timber to varnishing. In fact oak, chestnut, iroko, niangon, meranti, cedar, and hard exotic timbers with large pore generally contain inhibiting substances, which tend to leak if you use varnishing reducible by water. This inconvenience does not occur always and therefore it is difficult to explain it or to find a really effective remedy. If many tannin leaks occur (small black cylindrical “vulcanoes”), we suggest to sand the surface and apply a new layer of finish.
This material is flammable and must not be exposed to naked flames.
Use only in well ventilated areas. In case of insufficient ventilation during application wear suitable respiratory equipment. Do not breathe vapor / spray. In case of contact with eyes, rinse immediately with plenty of sweet water and seek medical advice. In case of contact with skin, wash immediately with soap and water or a recognized skin cleanser. Keep away from sources of ignition. No Smoking.
Keep out of reach of children.